The paper presents the results of operation of pilot batch of iron rolls manufactured via the method of centrifugal casting in dual-layer technique. Surface of roll barrel is cast of iron with high content of ledeburite alloyed with nickel, with fine laminar graphite and tempered beinite-martensite matrix, while core is made from spheroidized graphite. Wear resistance of iron rolls is higher compared with dteel rolls by 1.5 times.

1. Efimenko S. P.  Stal' - Steel. 1980. No. 8. pp. 730–733.
2. Belevskiy L. S., Ismagilov R. R., Moskvin V. M.  Vestnik MGTU im. G. I. Nosova - Journal of the Magnitogorsk State Technical University named after G. I. Nosov. 2010. No. 1. pp. 46–50.

3. Treyger E. I., Prikhod'ko V. P. and etc. Povyshenie kachestva i eksplutatsionnoy stoykosti valkov listovykh stanov (Improving the quality and operational stability of rolls of sheet mills).   Moscow: Metallurgiya, 1988. 192 p.
4. Forisenkov S. A., Lisitsyn S. P. Stal' dlya valkov kholodnoy prokatki (Steel rolls for cold rolling).  A. c. No. 186697. Bull. Inventions and Trademarks, 1966, No. 19.