ArticleName Combined effect of calcium and zinc on the hot cracking of Al – Mg аlloys
DOI 10.17580/tsm.2022.12.06
ArticleAuthor Doroshenko V. V., Barykin M. A., Vasina M. A., Aksenov A. A.
ArticleAuthorData

National University of Science and Technology MISiS, Moscow, Russia:

V. V. Doroshenko, Junior Researcher at the Laboratory for Catalysis and Hydrocarbons Processing, Candidate of Technical Sciences, e-mail: v.doroshenko@mail.ru
M. A. Barykin, Engineer at the Department of Metal Forming, Postgraduate Student
M. A. Vasina, Engineer at the Department of Metal Forming, Postgraduate Student
A. A. Aksenov, Professor at the Department of Metal Forming, Doctor of Technical Sciences

Abstract

This paper examines the effect of calcium and zinc on the hot cracking of cast magnaliums and how their hot cracking behaviour is related to their structure. The authors rely on the Thermo-Calc methods (TTAl5 database) to substantiate the composition of the Al – Mg – Ca – (Zn) alloys in view. Pure burden components were smelted in a resistance furnace and then cast in graphite and steel moulds. Structural and compositional analyses relied on optical and scanning electron microscopy. Specimens for structural and characterization studies were made out of flat castings with a 10×20 mm section, which were then remelted and cast into pencil-shaped specimens for hot cracking tests. It was found that as the concentration of calcium in the alloys rises, their eutectic becomes coarser, i.e. certain dendrite branches tend to get shorter and thicker. Combined inoculation with calcium and zinc does not modify the structure. A hot cracking study showed that a shorter crystallization interval applied when selecting an alloy did not impact that parameter in the studied system. For example, alloy Al – 10 Mg – 4 Ca has a shorter crystallization interval compared with alloy [АМг10ч]; at the same time the former is much more prone to hot cracking. Inoculating the experimental alloy Al – 6 Mg – 2 Ca – 2 Zn with zinc ensures a better resistance to hot cracking compared with the commercial alloy [АМг10ч]. A study that looked at the effect of superheating on castings showed that the best effect is achieved when heating 50 oC above the liquidus temperature. As the superheat temperature increases, so does the grain size of the Al – 6 Mg – 2 Ca – 2 Zn alloy. The hardness and density of this alloy are similar to those of the base one.
This research was funded by the Russian Science Foundation under Grant No. 21-79-00134.

keywords Аluminium, casting alloys, calcium, crystallization interval, microstructure, eutectic, hot cracking, hardness
References

1. Mallick P. K., Graf A. Materials, design and manufacturing for lightweight vehicles (2nd ed.). Cambridge, UK : Woodhead Publishing in Materials, 2020. 488 p.
2. Glazoff M. V., Khvan A. V., Zolotorevsky V. S., Belov N. A., Dinsdale A. T. Casting aluminum alloys. Their physical and mechanical metallurgy. Oxford, UK : Elsevier, 2019. 564 p.
3. Kaufman J. G., Rooy E. L. Aluminum Alloy Castings: Properties, Processes, and Applications. ASM International, 2004. 340 p.
4. Starke E. A., Staley J. T. Application of modern aluminum alloys to aircraft. Progress in Aerospace Sciences. 1996. Vol. 32, Iss. 2-3. pp. 131–172.
5. Mansurov Yu. N., Belov N. A., Sannikov A. V., Buravlev I. Yu. Optimization of composition and properties of heatresistant complex-alloyed aluminum alloy castings. Non-ferrous Metals. 2015. No. 2. pp. 48–55. DOI: 10.17580/nfm.2015.02.08.
6. Hatch J. E. Aluminum: Properties and Physical Metallurgy. Ohio : American Society for Metals, 1984. 424 p.
7. Zolotorevskiy V. S., Belov N. A. Metallurgy of aluminium casting alloys. Moscow : MISiS, 2005. 376 p.
8.GOST 1583–93.Aluminium casting alloys. Specifications. Introduced: 01.01.1997.
9. Mansurov Yu. N., Rakhmonov J. U., Letyagin N. V., Finogeyev A. S. Influence of impurity elements on the casting properties of Al – Mg based alloys. Non-ferrous Metals. 2018. No. 1. pp. 24–29.
10. Eskin D. G., Dr. Suyitno, Katgerman L. Mechanical properties in the semisolid state and hot tearing of aluminium alloys. Progress in Materials Science. 2004. Vol. 49. pp. 629–711.
11. Li J., Shi Q.-Y. Minimization of Welding Distortion and Buckling. Cambridge, UK : Woodhead Publishing in Materials, 2011. 298 p.
12. Matrukanitz R. P. Selection and weldability of heat-treatable aluminum alloys. ASM handbook: Welding brazing and soldering. 1993. Vol. 6. pp. 528–536.
13. Jia Z., Zhang P., Yu Z., Shi H. et al. Effect of pulse shaping on solidification process and crack in 5083 aluminum alloy by pulsed laser welding. Optics & Laser Technology. 2021. Vol. 134. pp. 106608–106611.
14. Li Y., Li H., Katgerman L., Du Q. et al. Recent advances in hot tearing during casting of aluminium alloys. Progress in Materials Science. 2021. Vol. 117. p. 100741.
15. Zuqi H., Li W., Shulin L., Peng Z., Shusen W. Research on the microstructure, fatigue and corrosion behavior of permanent mold and die cast aluminum alloy. Materials and Design. 2014. Vol. 55. pp. 353–360.

16. Weller D., Hagenlocher C., Steeb T., Weber R., Graf T. Self-restraint hot cracking test for aluminum alloys using digital image correlation. Procedia CIRP. 2018. Vol. 74. pp. 430–433.
17. OSTI 90020–71. Method for determining the hot tearing behavior of aluminium and magnesium casting alloys. Introduced: 06.04.1971.
18. Pozdnyakov A. V., Zolotorevskiy V. S., Khomutov M. G. Hot cracking of aluminium casting alloys : monograph. Moscow : MISiS, 2014. 88 p.
19. Naumova E. A., Belov N. A., Bazlova T. A. Effect of Heat treatment on structure and strengthening of cast eutectic aluminum alloy Al9Zn4Ca3Mg. Metal Science and Heat Treatment. 2015. Vol. 57, No. 5-6. pp. 274–280.
20. Belov N. A., Naumova E. A., Akopyan T. K. Eutectic alloys based on the Al – Zn – Mg – Ca system: microstructure, phase composition and hardening. Materials Science and Technology. 2017. Vol. 33, No. 6. pp. 656– 666.
21. Belov N. A., Akopyan T. K., Mishurov S. S., Korotkova N. O. Effect of Fe and Si on the microstructure and phase composition of the aluminium – calcium eutectic alloys. Non-ferrous Metals. 2017. No. 2. pp. 37–42. DOI: 10.17580/nfm.2015.02.08.
22. Shurkin P. K., Dolbachev A. P., Naumova E. A., Doroshenko V. V. Effect of iron on the structure, hardening and physical properties of the alloys of the Al – Zn – Mg – Ca system. Tsvetnye Metally. 2018. No. 5. pp. 69–77. DOI: 10.17580/tsm.2018.05.10.
23. Naumova E. A., Belov N. A., Vasina M. A., Doroshenko V. V. Substantiation of the choice of high-strength aluminium-calcium alloy. Tsvetnye Metally. 2019. No. 5. pp. 53–59. DOI: 10.17580/tsm.2019.05.06.
24. Belov N. A., Naumova E. A., Bazlova T. A., Alekseeva E. V. Aluminium casting alloys of the Al – Ca – Mg – Sc system: Structure, phase composition and hardening. Fizika metallov i metallovedenie. 2016. No. 2. pp. 196–203.
25. GOST 11069–2001. Primary aluminium. Grades. Introduced: 01.01.2003.
26. GOST 804–93. Primary magnesium ingots. Specifications. Introduced: 01.01.1997.
27. GOST 3640–94. Zinc. Specifications. Introduced: 01.01.1997.
28. Pikunov M. V. Melting of metals, crystallization of alloys, solidification of castings : A guide for university students. Moscow : MISiS, 1997. 376 p.
29. Pozdnyakov A. V. Calculation of a hot cracking parameter and its application for the development of new aluminium casting alloys: Candidate of Technical Sciences dissertation. Moscow, 2013. 123 p.
30. Polmear I. Light alloys: from traditional alloys to nanocrystals. 4th edition. Oxford : Elsevier, 2006. 421 p.
31. Mondolfo L. F. Aluminum alloys: Structure and properties. Translated from English. Moscow : Metallurgiya, 1979. 640 p.
32. Li Z. T., Qiao X. G., Xu C., Kamado S., Zheng M. Y., Luo A. A. Ultrahigh strength Mg – Al – Ca – Mn extrusion alloys with various aluminum contents. Journal of Alloys and Compounds. 2019. Vol. 792. pp. 130–141.
33. Novikov I. I. Hot cracking of non-ferrous metals and alloys. Moscow : Nauka, 1966. 300 p.
34. Kurdyumov A. V., Belov V. D., Pikunov M. V. et al. Production of castings out of non-ferrous metal alloys : textbook. Ed. by V. D. Belov. Moscow : MISiS, 2011. 615 p.

Language of full-text russian
Full content Buy
Back